EN-10270-3
| Tensile strength | |||||
| EN-10270-3 | WPB ( H ) | WPA | WPC | ||
| 1.4310 | 1.4401 (316) | 1.4568(631or 17-7) | |||
| Normal tenslle strength (NS)-min |
High tenslle strength (HS)-min |
(min) | (min) | ||
| ±0.008 | ≦0.20 | 2200 | 2350 | 1725 | 1975 |
| ±0.01 | >0.20 | 2150 | 2300 | 1700 | 1950 |
| ≦0.30 | |||||
| ±0.01 | >0.30 | 2100 | 2250 | 1675 | 1925 |
| ≦0.40 | |||||
| ±0.015 | >0.40 | 2050 | 2200 | 1650 | 1900 |
| ≦0.50 | |||||
| ±0.015 | >0.50 | 2000 | 2150 | 1625 | 1850 |
| ≦0.65 | |||||
| ±0.015 | >0.65 | 1950 | 2100 | 1600 | 1825 |
| ≦0.80 | |||||
| ±0.02 | >0.80 | 1900 | 2050 | 1575 | 1800 |
| ≦1.00 | |||||
| ±0.02 | >1.00 | 1850 | 2000 | 1550 | 1750 |
| ≦1.25 | |||||
| ±0.02 | >1.25 | 1800 | 1950 | 1500 | 1700 |
| ≦1.50 | |||||
| ±0.025 | >1.50 | 1750 | 1900 | 1450 | 1650 |
| ≦1.75 | |||||
| ±0.025 | >1.75 | 1700 | 1850 | 1400 | 1600 |
| ≦2.00 | |||||
| ±0.035 | >2.00 | 1650 | 1750 | 1350 | 1550 |
| ≦2.50 | |||||
| ±0.035 | >2.50 | 1600 | 1700 | 1300 | 1500 |
| ≦3.00 | |||||
| ±0.035 | 3.00 | 1550 | 1650 | 1250 | 1450 |
| ≦3.50 | |||||
| ±0.035 | >3.50 | 1500 | 1600 | 1225 | 1400 |
| ≦4.25 | |||||
| ±0.035 | >4.25 | 1450 | 1550 | 1200 | 1350 |
| ≦5.00 | |||||
| ±0.035 | >5.00 | 1400 | 1500 | 1150 | 1300 |
| ≦6.00 | |||||
| ±0.035 | >6.00 | 1350 | 1450 | 1125 | 1250 |
| ≦7.00 | |||||
| ±0.035 | >7.00 | 1300 | 1400 | 1075 | 1250 |
| ≦8.50 | |||||
| ±0.035 | >8.50 | 1250 | 1350 | 1050 | 1250 |
| ≦10.00 | |||||